Reference Number EP/N033930/1
Title Miniature Ultrasonic Fatigue Analysis of Local Modified Regions near Welds and Surfaces in Ti alloys
Status Completed
Energy Categories Nuclear Fission and Fusion(Nuclear Fission, Nuclear supporting technologies) 30%;
Not Energy Related 70%;
Research Types Basic and strategic applied research 100%
Science and Technology Fields PHYSICAL SCIENCES AND MATHEMATICS (Metallurgy and Materials) 100%
UKERC Cross Cutting Characterisation Not Cross-cutting 100%
Principal Investigator Dr AJ Wilkinson
No email address given
Materials
University of Oxford
Award Type Standard
Funding Source EPSRC
Start Date 01 June 2016
End Date 31 May 2019
Duration 36 months
Total Grant Value £486,814
Industrial Sectors Aerospace; Defence and Marine; Manufacturing
Region South East
Programme NC : Engineering
 
Investigators Principal Investigator Dr AJ Wilkinson , Materials, University of Oxford (100.000%)
  Industrial Collaborator Project Contact , Timet UK Ltd (0.000%)
Project Contact , Rolls-Royce PLC (0.000%)
Web Site
Objectives
Abstract Fatigue is a pervasive failure mode that affects many industrial sectors including the high value aerospace, nuclear and automotive sectors. It remains a source of in-service failure on the one hand and inefficient over-engineered conservative design on the other and so generates considerable risks and cost (capital and operating) to industry. In the lower stress regimes where high or very high cycles to failure occur there are several factors that complicate fundamental understanding of fatigue failure and how to manage it effectively in engineering practice:(i) testing methodologies generally only test to ~1 million cycles while safety critical components may see much longer service periods of a hundred to a thousand times longer in the aerospace and nuclear sector forcing extrapolation into unknown and untested regimes(ii) there is considerably more scatter in fatigue lives in (very) high cycle fatigue compared to low cycle fatigue which is linked to a greater influence of microstructure(iii) the crack initiation process takes up a much larger fraction of the total fatigue life but as no crack is present it is difficult to know where in the material microstructure to make observations that will capture local processes that will eventually lead to crack nucleation(iv) residual stresses from processing and machining make a more significant contribution to the total stress state when the external loading is smaller.This research programme will deliver a step change in high cycle fatigue testing by combining ultrasonic technology with small scale miniature test-piece designs.The tests will be conducted at 20 kHz at which a million cycles takes just less than a minute and a billion cycles takes only 1 day. The sample dimension will be in two regimes. Firstly, a micro-regime with Focused Ion Beam (FIB) cut sample widths only a fraction to a few micrometres across allowing testing of individual selected features of a microstructure (grain, grain boundary, inclusion...). Secondly, a meso-regime with samples a few tens to a few hundreds of micrometres wide cut using laser micro-machining and allowing small patches of microstructure to be tested. The meso-samples are sufficiently small that frequent intermittent microscopic characterisation methods can be used to the local evolution of local deformation, stress, and dislocation content in regions where crack initiation is guaranteed to occur eventually.Greater understanding of processes leading to crack initiation and how local variation in microstructure control fatigue crack initiation lifetimes are the key scientific and technological outcomes sought. This step change advance will be exploited in the first instance to characterize effects of process conditions on the fatigue crack initiation response of (i) linear friction welds & (ii) peened surfaces in Ti-6Al-4V